201 Stainless Steel Plate
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
201 Stainless Steel Plate Description
201 stainless steel is composed primarily of iron with between 16 and 18% chromium and up to 0.15% carbon. It also contains small amounts of manganese, nickel, silicon, nitrogen, and copper. It has higher formability than the 300 series grades. In addition, it can be hardened by cold working processes but not heat-treated like 304 or 316 grades. 201 is a high manganese and low nickel stainless steel with low nickel content and poor corrosion resistance. It is widely used in various tabletops, countertops, kitchenware, outdoor decoration engineering, urban decoration industry and low-grade household products. It is also used in medical instruments and automotive parts that require flexibility while maintaining strength under pressure.
Product Parameters
Product Name | 201 Stainless Steel Plate |
Type | Plate |
Thickness | 0.3mm-200mm |
Length | 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
Width | 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
Scope of Application | Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
Certificate | ISO, SGS, BV, etc. |
Production Technology | Hot Rolling, Cold Rolling |
Edge Processing | Edging, Trimming |
Chemical Composition
C | Si | Mn | Cr | Ni | S | P |
≤ 0.15 | ≤ 0.75 | 5.50~7.50 | 16.00~18.00 | 3.50~5.50 | ≤ 0.03 | ≤ 0.06 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥ 520 | ≥ 275 | ≥55-60 | ≤183HB；≤ 100 HRB |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(μohm.in) |
7.8 | 197 | 15.7 | 16.2 | 27 |