stainless steel
440C Stainless Steel Plate
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
440C Stainless Steel Plate Description
The high carbon content of 440C stainless steel makes it have good cutting and wear resistance. It also has excellent corrosion resistance and can resist the erosion of a variety of chemical corrosive media. 440C has excellent hardness due to its high carbon content. Through heat treatment and quenching, hardness of HRC 58-60 can be achieved, giving it excellent cutting ability and wear resistance. In addition, 440C has a high chromium content and excellent corrosion resistance in most acidic and alkaline environments. So 440C stainless steel material is especially suitable for high-end manufacturing fields such as aerospace, mechanical manufacturing, electronic equipment and medical devices.
Product Parameters
Product Name | 440C Stainless Steel Plate |
Type | Plate |
Thickness | 0.3mm-200mm |
Length | 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
Width | 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
Scope of Application | Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
Certificate | ISO, SGS, BV, etc. |
Production Technology | Hot Rolling, Cold Rolling |
Edge Processing | Edging, Trimming |
Chemical Composition
C | Si | Mn | Cr | S | P |
0.95～1.20 | ≤1.0 | ≤1.0 | 16.0～18.0 | ≤ 0.03 | ≤ 0.04 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥560 | ≥205 | ≥18 | ≤250HB |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.60 | 200 | 10.1 | 24.2 | 360 |
Surface Selection