stainless steel
305 Stainless Steel Plate
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
305 Stainless Steel Plate Description
305 stainless steel has good corrosion resistance and can remain stable in various corrosive media. The oxide film formed on its surface can effectively prevent the contact between the corrosive medium and the material, thereby extending the service life of the material. 305 stainless steel has good heat resistance and can maintain stable performance at high temperatures. Its high content of nickel element can improve the heat resistance of the material, making it less likely to deform, oxidize or fail at high temperatures. In addition, it has high strength and hardness and can withstand greater pressure and impact. Its high content of manganese element can improve the strength and hardness of the material, making it less likely to deform or break when under pressure. 305 stainless steel is often used in the chemical industry, food processing, construction, aerospace, marine engineering, and other fields.
Product Parameters
Product Name | 305 Stainless Steel Plate |
Type | Plate |
Thickness | 0.3mm-200mm |
Length | 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. |
Width | 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
Surface | BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. |
Scope of Application | Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. |
Certificate | ISO, SGS, BV, etc. |
Production Technology | Hot Rolling, Cold Rolling |
Edge Processing | Edging, Trimming |
Chemical Composition
C | Si | Mn | Cr | Ni | S | P |
≤ 0.04 | ≤ 0.75 | ≤ 2.0 | 17.0～19.0 | 10.5～13.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥515 | ≥205 | ≥35 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.99 | 193 | 17.3 | 16.2 | 72 |
Surface Selection