254SMO Stainless Steel Bar
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
254SMO Stainless Steel Bar Description
254SMO stainless steel bars are made from a highly corrosion-resistant austenitic stainless steel. They are mainly used in high-concentration chloride ion environments and highly corrosive media, such as seawater, salt water, wet chlorine, acetic acid, formic acid, acetic acid, sulfuric acid, nitric acid, etc.. On the other hand, they have good processing performance and welding performance. With high content of chromium and molybdenum, such bars are very resistant to pitting and crevice corrosion. Since this special stainless steel is a high-alloy material, the manufacturing process is quite complex. Generally, only traditional processes can be implemented to manufacture this special stainless steel, such as pouring, forging, rolling, etc.
Product Parameters
Product Name | 254SMO Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | Mo | S | P |
≤ 0.02 | ≤ 0.8 | ≤ 1.0 | 19.5~20.5 | 17.5~18.5 | 6.0~6.5 | ≤ 0.01 | ≤ 0.03 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥680 | ≥300 | ≥45 | ≤ 180HRB |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
8.0 | 195 | 16.0 | 14.0 | 85 |