904L Stainless Steel Bar
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
904L Stainless Steel Bar Description
904L stainless steel bars are made of a high-strength material. This high-strength characteristic allows the bars to show stable performance when subjected to high loads and stresses, and is not prone to deformation and fracture. Besides, good toughness and can help maintain stable performance in low temperature environments. More importantly, 904L stainless steel bars can maintain good durability and stability in friction and wear environments. This characteristic allows 904L stainless steel bars to have a long service life under mechanical movements and friction situations. Lastly, 904L stainless steel bars can maintain stable performance in various corrosive environments.
Product Parameters
Product Name | 904L Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | Mo | S | P |
≤ 0.02 | ≤1.0 | ≤ 2.0 | 19.0～23.0 | 23.0～28.0 | 4.0～5.0 | ≤ 0.035 | ≤ 0.045 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥490 | ≥220 | ≥35 | ≤ 90HRB |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
8.0 | 195 | 15.5 | 12.0 | 94 |