420 Stainless Steel Bar Description
420 stainless steel bar is a medium carbon stainless steel. Under normal circumstances, 420 stainless steel has rather limited heat resistance and is favored for low-temperature working environments. Its maximum operating temperature is usually 650°C. Certain heat treatment processes, such as solution treatment and quenching and annealing are usually implemented to improve the heat resistance of 420 stainless steel by improving the material's grain boundary structure and grain size. The heat resistance of 420 stainless steel is lower than other heat-resistant stainless steels. So 420 stainless steel bars are not the perfect option for high temperature uses.
Product Parameters
Product Name | 420 Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | S | P |
≤ 0.15 | ≤1.0 | ≤1.0 | 12.0～14.0 | ≤ 0.03 | ≤ 0.04 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥634 | ≥440 | ≥20 | Annealing≤ 223HB; quenching and tempering ≥ 192HB |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.74 | 200 | 10.2 | 24.9 | 55 |