305 Stainless Steel Bar
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
305 Stainless Steel Bar Description
305 stainless steel bar has good corrosion resistance and can remain stable in various corrosive media. The oxide film formed on its surface can effectively prevent the contact between the corrosive medium and the material, thereby extending the service life of the material. 305 stainless steel bars have good heat resistance and can maintain stable performance at high temperatures owing to its high content of nickel element, making it less likely to deform, oxidize or fail at high temperatures. In addition, it can withstand greater pressure and impact with better hardness and strength as a result of its high content of manganese, making it less likely to deform or break when under pressure. 305 stainless steel bars are often used as manufacturing parts in the chemical industry, food processing, construction, aerospace, marine engineering.
Product Parameters
Product Name | 305 Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | S | P |
≤ 0.04 | ≤ 0.75 | ≤ 2.0 | 17.0～19.0 | 10.5～13.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥515 | ≥205 | ≥35 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.99 | 193 | 17.3 | 16.2 | 72 |