316 Stainless Steel Bar Description
316 stainless steel bar has a number of convincing reasons to be used as a very practical option. Grade 316 is highly resistant to pitting and crevice corrosion in chloride environments as a standard molybdenum-bearing austenitic grade. So it is more commonly used in situations where higher corrosion resistance is asked. For example, in marine engineering, 316 stainless steel is often used to produce ship parts, subsea pipelines, offshore platforms and other facilities. Chemical industry is also where it is adopted. In addition, in the medical field, 316 stainless steel bars are sometimes used to manufacture medical devices and implants due to its excellent biocompatibility and corrosion resistance.
Product Parameters
Product Name | 316 Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | S | P | Mo |
≤ 0.03 | ≤ 0.75 | ≤ 2.0 | 16.0～18.0 | 10.0～14.0 | ≤ 0.03 | ≤ 0.045 | 2.0～3.0 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥480 | ≥177 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.99 | 193 | 16.0 | 16.2 | 74 |