403 Stainless Steel Bar
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
403 Stainless Steel Bar Description
403 stainless steel bars are suitable for use in harsh environments given its good corrosion resistance. Additionally, they also have good mechanical properties, including high hardness, toughness and wear resistance. One thing to note is such bars are not as resistant to corrosion as other stainless steels such as 304 or 316 and may not be suitable for use in extremely corrosive environments. The Nickel element enables 403 stainless steel to obtain a complete austenite structure, providing the steel with higher strength, plasticity and toughness, as well as excellent hot and cold workability, cold formability, weldability. Additionally, it improves the thermodynamic stability of 403 stainless steel.
Product Parameters
Product Name | 403 Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | S | P |
≤ 0.15 | ≤ 0.5 | ≤1.0 | 11.5～13.0 | ≥ 0.6 | ≤ 0.03 | ≤ 0.04 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥485 | ≥290 | ≥25 | ≤ 98HRB |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(10-6 Ω.m) |
7.80 | 190 | 9.9 | 21.5 | 740 |