316L Stainless Steel Bar
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
316L Stainless Steel Bar Description
316L stainless steel bar just has a lower carbon content than 316 stainless steel bar and it is used mostly for welding purposes. The lower carbon content greatly lowers the precipitation of carbides in the heat-affected zone close to the weld, and such precipitation is likely to lead to intergranular corrosion of stainless steel in certain settings. Basically, their is no need to anneal weld joints prior to using the completed metal form using 304L, which helps save time and effort. 316L stainless steel bar is one of the most widely used stainless steel bars like 304, with better corrosion resistance. 316L stainless steel bar also has high temperature resistance that can go with up to 1000 degrees. Lastly, 316L stainless steel has stronger rust resistance than 200 series stainless steel materials.
Product Parameters
Product Name | 316L Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | S | P | Mo |
≤ 0.03 | ≤1.0 | ≤ 2.0 | 16.0～18.0 | 10.0～14.0 | ≤ 0.03 | ≤ 0.045 | 2.0～3.0 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥480 | ≥177 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.99 | 193 | 16.0 | 16.2 | 74 |