2205 Duplex Stainless Steel Bar Description
2205 Duplex stainless steel bars have more than twice of yield strength than ordinary austenitic stainless steel, and it has enough plastic toughness for molding. Moreover, it has good local corrosion resistance, and compared with austenitic stainless steel with similar alloy content, its wear corrosion resistance and fatigue corrosion performance are better than austenitic stainless steel. Whether under dynamic load or static load conditions, 2205 duplex stainless steel bars have a higher energy absorption capacity than austenitic stainless steel, which is why they have obvious advantages for structural parts to cope with emergencies such as collisions, explosions, etc..
Product Parameters
Product Name | 2205 Duplex Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | Mo | S | P |
≤ 0.03 | ≤ 1.0 | ≤ 2.0 | 21.0～23.0 | 4.5～6.5 | 2.5～3.5 | ≤ 0.02 | ≤ 0.03 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥620 | ≥450 | ≥25 | ≤ 293HB |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.88 | 190 | 13.7 | 19.0 | 80 |