stainless steel
317L Stainless Steel Bar
We ensure that every product we offer meets the highest standards of quality and reliability. Factory test certification is included with the shipment and third party inspection is available.
We provide comprehensive steel processing services such as cutting, bending, welding, and finishing.
Customizable: Available in various sizes and thicknesses to meet specific project requirements. Free samples are available, Customized samples will take about 5-7days. Customized logo , Customized packaging , Product customization.
Our location is Wuxi, Jiangsu, China
317L Stainless Steel Bar Description
The chemical composition of 317L stainless steel bars leads to the unique properties and characteristics. This type of stainless steel is composed of a combination of elements such as chromium, nickel, molybdenum, and carbon. Chromium is the most substantial component of 317L stainless steel and makes for its exceptional corrosion resistance. It helps form a protective layer on the metal surface, preventing rust and staining. Molybdenum is associated with better resistance to pitting corrosion from chloride solutions commonly found in harsh environments such as seawater or chemical processing plants. Carbon content helps increase hardness and strength. 317L stainless steel bars perform better than traditional austenitic grades when used in high-temperature, corrosive environments because of the precise balance between these elements.
Product Parameters
Product Name | 317L Stainless Steel Bar | |
Type | Steel Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
C | Si | Mn | Cr | Ni | S | P | Mo |
≤ 0.035 | ≤ 0.75 | ≤ 2.0 | 18.0～20.0 | 11.0～15.0 | ≤ 0.03 | ≤ 0.04 | 3.0～4.0 |
Mechanical Properties
Tensile StrengthKb (MPa) | Yield Strengthσ0.2 (MPa) | ElongationD5 (%) | Hardness |
≥480 | ≥177 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
7.99 | 193 | 16.0 | 16.2 | 79 |